Diamond simulant
1608081
219407949
2008-06-15T02:16:41Z
Lightbot
7178666
Units/dates/other
:''This article addresses the many imitations of diamond. For a broader discussion of diamonds, see '''[[diamond]]'''. For other uses of the word diamond, see [[diamond (disambiguation)]].''
[[Image:CZ brilliant.jpg|right|frame|Due to its low cost and close visual likeness to diamond, [[cubic zirconia]] has remained the most gemologically and economically important diamond simulant since 1976.]]
The high price of [[gemstone|gem]]-grade [[diamond]]s has created a large demand for materials with similar [[gemology|gemological]] characteristics, known as '''diamond simulants''' or '''imitations'''. Simulants are distinct from [[synthetic diamond]], which unlike simulants is actual diamond, and therefore has the same [[material properties of diamond|material properties]] as natural diamond. [[Diamond enhancement|Enhanced diamonds]] are also excluded from this definition. A diamond simulant may be artificial, natural, or in some cases a combination thereof. While their material properties depart markedly from those of diamond, simulants have certain desired characteristics—such as [[dispersion (optics)|dispersion]] and [[hardness]]—which lend themselves to imitation. Trained gemologists with appropriate equipment are able to distinguish natural and synthetic diamonds from all diamond simulants, primarily by visual inspection.
The most common diamond simulants are high-[[leaded glass]] (i.e., [[rhinestone]]s) and [[cubic zirconia]] (CZ), both artificial materials. A number of other artificial materials, such as [[strontium titanate]] and synthetic [[rutile]] have been developed since the mid 1950s, but these are no longer in common use. Introduced at the end of the 20th century, the lab grown product [[moissanite]] has gained popularity as an alternative to diamond.
== Desired and differential properties ==
{{seealso|Material properties of diamond}}
In order to be considered for use as a diamond simulant, a material must possess certain diamond-like properties. The most advanced artificial simulants have properties which closely approach diamond, but all simulants have one or more features that clearly and (for those familiar with diamond) easily differentiate them from diamond. To a [[gemologist]], the most important of differential properties are those that foster non-destructive testing, and most of these are visual in nature. Non-destructive testing is preferred because most suspected diamonds are already cut into gemstones and set in [[jewelry]], and if a destructive test (which mostly relies on the relative fragility and softness of non-diamonds) fails it may damage the simulant—this is not an acceptable outcome for most jewelry owners, as even if a stone is not a diamond it may still be of value.
Following are some of the properties by which diamond and its simulants can be compared and contrasted.
=== Durability and density ===
The [[Mohs scale of mineral hardness]] is a non-linear scale of common [[minerals]]' resistances to scratching. Diamond is at the top of this scale (hardness 10) as it is the [[hardness|hardest]] naturally occurring material known (the hardest substance known today is the man-made substance [[aggregated diamond nanorods]]). Since diamonds are unlikely to encounter substances that can scratch it, other than another diamond, diamond gemstones are typically free of scratches. Diamond's hardness also is visually evident (under the [[microscope]] or [[loupe]]) by its highly [[Lustre (mineralogy)|lustrous]] [[facet]]s (described as ''adamantine'') which are perfectly flat, and its crisp, sharp facet edges. For a diamond simulant to be effective, it must be very hard relative to most gems. Most simulants fall far short of diamond's hardness, so they can be separated from diamond by their external flaws and poor polish.
In the recent past, the so-called "window pane test" was commonly thought to be an assured method of identifying diamond. It is a potentially destructive test wherein a suspect diamond gemstone is scraped against a pane of glass, with a positive result being a scratch on the glass and none on the gemstone. The use of [[hardness point]]s and [[scratch plate]]s made of [[corundum]] (hardness 9) are also used in place of glass. Hardness tests are inadvisable for three reasons: glass is fairly soft (typically 6 or below) and can be scratched by a large number of materials (including many simulants); diamond has four directions of perfect and easy [[Cleavage (crystal)|cleavage]] (planes of structural weakness along which the diamond could split) which could be triggered by the testing process; and many diamond-like gemstones (including older simulants) are valuable in their own right.
The [[specific gravity]] (SG) or density of a gem diamond is fairly constant at 3.52. Most simulants are far above or slightly below this value, which can make them easy to identify if unset. High-density liquids such as [[diiodomethane]] can be used for this purpose, but they are all highly [[toxin|toxic]] so are usually avoided. A more practical method is to compare the expected size and weight of a suspect diamond to its measured parameters: for example, a [[cubic zirconia]] (SG 5.6–6) will be 1.7 times the expected weight of an equivalently sized diamond.
=== Optics and color ===
Diamonds are usually cut into [[brilliant (diamond cut)|brilliant]]s to bring out their ''brilliance'', the amount of light reflected back to the viewer, and ''fire'', the degree of colorful [[prism (optics)|prismatic]] flashes seen. Both properties are strongly affected by the cut of the stone, but they are a function of diamond's high [[refractive index]] (RI; the degree to which incident light is bent upon entering the stone) of 2.417 (as measured by [[sodium light]], 589.3 nm) and high [[dispersion (optics)|dispersion]] (the degree to which white light is split into its [[spectral color]]s within the stone) of 0.044, as measured by the sodium B and G line interval. Thus, if a diamond simulant's RI and dispersion are too low it will appear comparatively dull or "lifeless"; if the RI and dispersion are too high, the effect will be considered unreal or even tacky. Very few simulants have closely approximating RI and dispersion, but even the close simulants can be separated by an experienced observer. Direct measurements of RI and dispersion are impractical (a standard gemological [[refractometer]] has an upper limit of about RI 1.81), but several companies have devised [[reflectivity]] meters to gauge a material's RI indirectly by measuring how well it reflects an [[infrared]] beam.
Perhaps equally as important is ''optic character''. Diamond and other [[cubic (crystal system)|cubic]] (and also [[amorphous]]) materials are ''[[isotropic]]'', meaning light entering a stone behaves the same way regardless of direction. Conversely, most minerals are ''[[anisotropic]]'' which produces [[birefringence]] or double refraction of light entering the material in all directions other than an [[optic axis]] (a direction of single refraction in a doubly refractive material). Under low magnification, this birefringence is usually detectable as a visual doubling of a cut gemstone's rear facets or internal flaws. An effective diamond simulant should therefore be isotropic.
Under longwave (365 nm) [[ultraviolet]] light, diamond may [[fluorescence|fluoresce]] a blue, yellow, green, mauve, or red of varying intensity. The most common fluorescence is blue, and such stones may also [[phosphorescence|phosphoresce]] yellow—this is thought to be a unique combination among gemstones. There is usually little if any response to shortwave ultraviolet, in contrast to many diamond simulants. Similarly, because most diamond simulants are artificial they tend to have uniform properties: in a multi-stone diamond ring, one would expect the individual diamonds to fluoresce differently (in different colors and intensities, with some likely to be inert). If all the stones fluoresce in an identical manner, they are unlikely to be diamond.
Most "colorless" diamonds are actually tinted yellow or brown to some degree, whereas artificial simulants are usually completely colorless—the equivalent of a perfect "D" in [[diamond color]] terminology. This "too good to be true" factor is important to consider; colored diamond simulants meant to imitate fancy diamonds are more difficult to spot in this regard, but the simulants' colors rarely approximate. In most diamonds (even colorless ones) a characteristic [[absorption spectrum]] can be seen (via a direct-vision [[spectroscope]]), consisting of a fine line at 415 nm. The [[dopant]]s used to impart color in artificial simulants may be detectable as a complex [[Rare earth element|rare earth]] absorption spectrum, which is never seen in diamond.
Also present in most diamonds are certain internal and external flaws or ''inclusions'', the most common of which are fractures and solid foreign crystals. Artificial simulants are usually internally flawless, and any flaws that are present are characteristic of the manufacturing process. The inclusions seen in natural simulants will often be unlike those ever seen in diamond, most notably [[liquid]] "feather" inclusions. The [[diamond cutting]] process will often leave portions of the original crystal's surface intact. These are termed ''naturals'' and are usually on the girdle of the stone; they take the form of triangular, rectangular, or square pits (''etch marks'') and are seen only in diamond.
=== Thermal and electrical ===
Diamond is an extremely effective [[thermal conductivity|thermal conductor]] and usually an [[electricity|electrical]] [[Electrical insulation|insulator]]. The former property is widely exploited in the use of an electronic ''thermal probe'' to separate diamonds from their imitations. These probes consist of a pair of battery-powered [[thermistor]]s mounted in a fine [[copper]] tip. One thermistor functions as a [[heat]]ing device while the other measures the temperature of the copper tip: if the stone being tested is a diamond, it will conduct the tip's thermal energy rapidly enough to produce a measurable temperature drop. As most simulants are thermal insulators, the thermistor's heat will not be conducted. This test takes about 2–3 seconds. The only possible exception is [[moissanite]], which has a thermal conductivity similar to diamond: older probes can be fooled by moissanite, but newer testers are sophisticated enough to differentiate the two materials.{{Fact|date=December 2007}}
A diamond's electrical conductance is only relevant to blue or gray-blue stones, because the interstitial [[boron]] responsible for their color also makes them [[semiconductor]]s. Thus a suspected blue diamond can be affirmed if it completes an [[electric circuit]] successfully.
== Artificial simulants ==
Diamond has been imitated by artificial materials for hundreds of years: advances in technology have seen the development of increasingly better simulants with properties ever nearer those of diamond. Although most of these simulants were characteristic of a certain time period, their large production volumes ensured that all continue to be encountered with varying frequency in jewelry of the present. Nearly all were first conceived for intended use in [[high technology]], such as [[lasing medium]]s, [[varistor]]s, and [[bubble memory]]. Due to their limited present supply, collectors may pay a premium for the older types.
===Summary table===
{| class="wikitable"
|+'''Diamond simulants and their gemological properties'''
|-
! Material
! Formula
! [[Refractive index|Refractive<BR>index(es)]]<BR>589.3 nm
! [[Dispersion (optics)|Dispersion]]<BR>431 - 687 nm
! [[Hardness]]<BR>([[Mohs scale of mineral hardness|Mohs'<BR>scale]])
! [[Specific gravity|Density]]<BR>(g/cm<SUP>3</SUP>)
! [[Thermal conductivity|Thermal<BR>Cond.]]
! State of<BR>the art
|-
! [[Diamond]]
| C
| 2.417
| 0.044
| 10
| 3.52
| Excellent
| 1476 –
|-
! colspan="8" align="left"| Artificial Simulants:
|-
! [[Glass]]es
| [[Silica]] with [[Lead|Pb]], [[Aluminum|Al]], &/or [[Thallium|Tl]]
| ~ 1.6
| > 0.020
| < 6
| 2.4 – 4.2
| Poor
| 1700 –
|-
! White [[Sapphire]]
| Al<SUB>2</SUB>O<SUB>3</SUB>
| 1.762 – 1.770
| 0.018
| 9
| 3.97
| Poor
| 1900 – 1947
|-
! [[Spinel]]
| MgO·Al<SUB>2</SUB>O<SUB>3</SUB>
| 1.727
| 0.020
| 8
| ~ 3.6
| Poor
| 1920 – 1947
|-
! [[Rutile]]
| TiO<SUB>2</SUB>
| 2.62 – 2.9
| 0.33
| ~ 6
| 4.25
| Poor
| 1947 – 1955
|-
! [[Strontium titanate]]
| SrTiO<SUB>3</SUB>
| 2.41
| 0.19
| 5.5
| 5.13
| Poor
| 1955 – 1970
|-
! [[YAG]]
| Y<SUB>3</SUB>Al<SUB>5</SUB>O<SUB>12</SUB>
| 1.83
| 0.028
| 8.25
| 4.55 – 4.65
| Poor
| 1970 – 1975
|-
! [[Gadolinium gallium garnet|GGG]]
| Gd<SUB>3</SUB>Ga<SUB>5</SUB>O<SUB>12</SUB>
| 1.97
| 0.045
| 7
| 7.02
| Poor
| 1973 – 1975
|-
! [[Cubic zirconia|Cubic Zirconia]]
| ZrO<SUB>2</SUB>(+ rare earths)
| ~ 2.2
| ~ 0.06
| ~ 8.3
| ~ 5.7
| Poor
| 1976 –
|-
! [[Moissanite]]
| SiC
| 2.648 – 2.691
| 0.104
| 8.5-9.25
| 3.2
| High
| 1998 –
|}
The "refractive index(es)" column shows one refractive index for singly refractive substances, and a range for doubly refractive substances.
=== 1700 onwards ===
The formulation of [[glass]]es using [[lead]], [[alumina]], and [[thallium]] to increase RI and dispersion began in the late [[Baroque]] period. These glasses are fashioned into [[brilliant (diamond cut)|brilliant]]s, and when freshly cut they can be surprisingly effective diamond simulants. Known as rhinestones, pastes, or strass, glass simulants are a common feature of [[antique]] [[jewelry]], and in such cases rhinestones can be valuable historical artifacts in their own right. The great softness (below hardnes 6) imparted by the lead means a rhinestone's facet edges and faces will quickly become rounded and scratched. Together with [[conchoidal fracture]]s, and air bubbles or flow lines within the stone, these features make glass imitations easy to spot under only moderate magnification. In contemporary production it is more common for glass to be molded rather than cut into shape: in these stones the facets will be concave and facet edges rounded, and mold marks or seams may also be present. Glass has also been combined with other materials to produce [[#Composites|composites]].
=== 1900–1947 ===
The first [[crystal]]line artificial diamond simulants were synthetic white [[sapphire]] ([[aluminium|Al]]<sub>2</sub>O<sub>3</sub>, pure [[corundum]]) and [[spinel]] (MgO·Al<sub>2</sub>O<sub>3</sub>, pure [[magnesium]] aluminium [[oxide]]). Both have been synthesized in large quantities since the first decade of the 20th century via the [[Verneuil process|Verneuil]] or flame-fusion process, although spinel was not in wide use until the 1920s. The Verneuil process involves an inverted [[oxyhydrogen flame|oxyhydrogen]] [[blowpipe]], with purified feed powder mixed with [[oxygen]] that is carefully fed through the blowpipe. The feed powder falls through the oxy-hydrogen flame, melts, and lands on a rotating and slowly descending pedestal below. The height of the pedestal is constantly adjusted to keep its top at the optimal position below the flame, and over a number of hours the molten powder cools and crystallizes to form a single pedunculated pear or ''[[boule (crystal)|boule]]'' crystal. The process is an economical one, with crystals of up to 9 centimeters (3.5 inches) in diameter grown. Boules grown via the modern [[Czochralski process]] may weigh several kilograms.
Synthetic sapphire and spinel are durable materials (hardness 9 and 8) that take a good polish, but due to their much lower RI when compared to diamond (1.762–1.770 for sapphire, 1.727 for spinel) they are "lifeless" when cut. (Synthetic sapphire is also anisotropic, making it even easier to spot.) Their low RIs also mean a much lower dispersion (0.018 and 0.020), so even when cut into brilliants they lack the ''fire'' of diamond. Nevertheless synthetic spinel and sapphire were popular diamond simulants from the 1920s up until the late 1940s, when newer and better simulants began to appear. Both have also been combined with other materials to create [[#Composites|composites]]. Commercial names once used for synthetic sapphire include ''Diamondette'', ''Diamondite'', ''Jourado Diamond''', and ''Thrilliant''. Names for synthetic spinel included ''Corundolite'', ''Lustergem'', ''Magalux'', and ''Radient''.
=== 1947–1970 ===
The first of the optically "improved" simulants was synthetic [[rutile]] (TiO<sub>2</sub>, pure [[titanium]] oxide). Introduced in 1947–48, synthetic rutile possesses plenty of life when cut—perhaps too much life for a diamond simulant. Synthetic rutile's RI and dispersion (2.8 and 0.33) are so much higher than diamond that the resultant brilliants look almost [[opal]]-like in their display of prismatic colors. Synthetic rutile is also doubly refractive: although some stones are cut with the table perpendicular to the optic axis to hide this property, merely tilting the stone will reveal the doubled back facets.
The continued success of synthetic rutile was also hampered by the material's inescapable yellow tint, which producers were never able to remedy. However, synthetic rutile in a range of different colors, including blues and reds, were produced using various metal oxide [[dopant]]s. These and the near-white stones were extremely popular if unreal stones. Synthetic rutile is also fairly soft (hardness ~6) and brittle, and therefore wears poorly. It is synthesized via a modification of the Verneuil process, which uses a third oxygen pipe to create a ''tricone burner''—this is necessary to produce a single crystal, due to the much higher oxygen losses involved in the oxidation of titanium. The technique was invented by Charles H. Moore, Jr. at the [[South Amboy, New Jersey|South Amboy]], [[New Jersey]]-based National Lead Company (later N. L. Industries). National Lead and [[Union Carbide]] were the primary producers of synthetic rutile, and peak annual production reached 750,000 carats (150 kg). Some of the many commercial names applied to synthetic rutile include: ''Astryl'', ''Diamothyst'', ''Gava'' or ''Java Gem'', ''Meredith'', ''Miridis'', ''Rainbow Diamond'', ''Rainbow Magic Diamond'', ''Rutania'', ''Titangem'', ''Titania'', and ''Ultamite''.
National Lead was also where research into the synthesis of another titanium compound, [[strontium titanate]] ([[Strontium|Sr]]TiO<sub>3</sub>, pure tausonite), was conducted. Research was done during the late 1940s and early 1950s by Leon Merker and Langtry E. Lynd, who also used a tricone modification of the Verneuil process. Upon its commercial introduction in 1955, strontium titanate quickly replaced synthetic rutile as the most popular diamond simulant. This was due not only to strontium titanate's novelty, but to its superior optics: its RI (2.41) is very close to that of diamond, while its dispersion (0.19), although also very high, was a significant improvement over synthetic rutile's psychedelic display. Perhaps most importantly was the complete lack of yellow tint that so plagued synthetic rutile. Dopants were also used to give synthetic titanate a variety of colors, including yellow, orange to red, blue, and black. The material is also [[isotropic]] like diamond, meaning there is no distracting doubling of facets as seen in synthetic rutile.
Strontium titanate's only major drawback (if one excludes excess fire) is fragility. It is both softer (hardness 5.5) and more brittle than synthetic rutile—for this reason, strontium titanate was also combined with more durable materials to create [[#Composites|composites]]. It was otherwise the best simulant around at the time, and at its peak annual production was 1.5 million carats (300 kg). Due to [[patent]] coverage all [[United States|US]] production was by National Lead, while large amounts were produced overseas by [[Nakazumi Company]] of [[Japan]]. Commercial names for strontium titanate included ''Brilliante'', ''Diagem'', ''Diamontina'', ''Fabulite'', and ''Marvelite''.
=== 1970–1976 ===
From about 1970 strontium titanate began to be replaced by a new class of diamond imitations: the "synthetic [[garnet]]s." These are not true garnets in the usual sense because they are [[oxide]]s rather than [[silicate]]s, but they do share natural garnet's [[crystal structure]] (both are cubic and therefore isotropic) and the general formula A<sub>3</sub>B<sub>2</sub>C<sub>3</sub>O<sub>12</sub>. While in natural garnets C is always [[silicon]] and A and B may be one of several common [[Chemical element|element]]s, most synthetic garnets are composed of uncommon [[rare earth element]]s. They are the only diamond simulants (aside from rhinestones) with no known natural counterparts: gemologically they are best termed ''artificial'' rather than ''synthetic'', because the latter term is reserved for human-made materials that can also be found in nature.
Although a number of artificial garnets were successfully grown, only two became important as diamond simulants. The first was [[yttrium aluminium garnet]] ([[YAG]]; Y<sub>3</sub>Al<sub>5</sub>O<sub>12</sub>) in the late 1960s. It was (and still is) produced via the Czochralski or crystal-pulling process, which involves growth from the melt. An [[iridium]] [[crucible]] surrounded by an [[inert]] atmosphere is used, wherein [[yttrium]] oxide and [[aluminium]] oxide are melted and mixed together at a carefully controlled temperature of ca. 1980°C. A small seed crystal is attached to a rod which is lowered over the crucible until the crystal contacts the surface of the melted mixture. The seed crystal acts as a site of [[nucleation]]; the temperature is kept steady at a point where the surface of the mixture is just below the melting point. The rod is slowly and continuously rotated and retracted, and the pulled mixture crystallizes as it exits the crucible, forming a single crystal in the form of a cylindrical boule. The crystal's purity is extremely high, and it typically measures 5 cm (2 inches) in diameter and 20 cm (8 inches) long, and weighs 9,000 carats (1.75 kg).
YAG's hardness (8.25) and lack of brittleness were great improvements over strontium titanate, and although its RI (1.83) and dispersion (0.028) were fairly low, they were enough to give brilliant-cut YAGs perceptible fire and good brilliance (although still much lower than diamond). A number of different colors were also produced with the addition of dopants, including yellow, red, and a vivid green which was used to imitate [[emerald]]. Major producers included [[ICT, INC.]] of Michigan, [[Litton Systems]], [[Allied Chemical]], [[Raytheon]], and [[Union Carbide]]; annual global production peaked at 40 million carats (8,000 kg) in 1972, but fell sharply thereafter. Commercial names for YAG included ''Diamonair'', ''Diamonique'', ''Gemonair'', ''Replique'', and ''Triamond''.
While market saturation was one reason for the fall in YAG production levels, another was the recent introduction of the other artificial garnet important as a diamond simulant, [[gadolinium gallium garnet]] (GGG; Gd<sub>3</sub>Ga<sub>5</sub>O<sub>12</sub>). Produced in much the same manner as YAG (but with a lower melting point of 1750°C), GGG had an RI (1.97) close to, and a dispersion (0.045) nearly identical to diamond. GGG was also hard enough (hardness 7) and tough enough to be an effective gemstone, but its ingredients were also much more expensive than YAG's. Equally hindering was GGG's tendency to turn a dark brown upon exposure to [[sunlight]] or other [[ultraviolet]] source: this was due to the fact that most GGG gems were fashioned from impure material that was rejected for technological use. The SG of GGG (7.02) is also the highest of all diamond simulants and amongst the highest of all gemstones, which makes loose GGG gems easy to spot by comparing their dimensions with their expected and actual weights. Relative to its predecessors, GGG was never produced in significant quantities; it became more or less unheard of by the close of the 1970s. Commercial names for GGG included ''Diamonique II'' and ''Galliant''.
=== 1976 to present ===
[[Cubic zirconia]] or CZ (ZrO<sub>2</sub>; [[zirconium]] oxide—not to be confused with [[zircon]], a zirconium silicate) quickly dominated the diamond simulant market following its introduction in 1976, and it remains the most gemologically and economically important simulant. CZ had been synthesized since 1930 but only in [[ceramic]] form: the growth of single-crystal CZ would require an approach radically different from those used for previous simulants due to zirconium's extremely high melting point (2750°C), unsustainable by any [[crucible]]. The solution found involved a network of water-filled copper pipes and [[radio frequency induction]] coils; the latter to heat the zirconium feed powder, and the former to cool the exterior and maintain a retaining "skin" under 1 millimeter thick. CZ was thus grown in a crucible of itself, a technique called ''cold crucible'' (in reference to the cooling pipes) or ''[[skull crucible]]'' (in reference to either the shape of the crucible or of the crystals grown).
At [[standard conditions for temperature and pressure|standard pressure]] zirconium oxide would normally crystallize in the [[monoclinic]] rather than cubic crystal system: for cubic crystals to grow, a stabilizer must be used. This is usually [[yttrium]] or [[calcium]]. The skull crucible technique was first developed in 1960s [[France]], but it was perfected in the early 1970s by [[Soviet]] scientists under V. V. Osiko at the [[Lebedev Physical Institute]] in [[Moscow]]. By 1980 annual global production had reached 50 million carats (10,000 kg).
The hardness (8–8.5), RI (2.15–2.18, isotropic), dispersion (0.058–0.066), and low material cost make CZ the best and most popular simulant of diamond. Its optical and physical constants are however variable, owing to the different stabilizers used by different producers. It is important to realize that CZ is not a compound. There are many formulations of stabilized cubic zirconia. These variations change the physical and optical properties markedly. While the visual likeness of CZ is close enough to diamond to fool most who do not handle diamond regularly, CZ will usually give certain clues. For example: it is somewhat brittle and is soft enough to possess scratches after normal use in jewelry; it is usually internally flawless and completely colorless (whereas most diamonds have some internal imperfections and a yellow tint); its SG (5.6–6) is high; and its reaction under [[ultraviolet]] light is a distinctive beige. Most jewelers will use a thermal probe to test all suspected CZs, a test which relies on diamond's superlative [[thermal conductivity]] (CZ, like almost all other diamond simulants, is a thermal [[Electrical insulation|insulator]]). CZ is made in a number of different colors meant to imitate fancy diamonds (e.g., yellow to golden brown, orange, red to pink, green, and opaque black), but most of these do not approximate the real thing. Some CZs have been given a coating of [[diamond-like carbon]] in an effort to improve their durability, but this does not fool a thermal probe.
CZ had virtually no competition until the 1998 introduction of simulated [[moissanite]] (SiC; synthetic silicon carbide). Simulated moissanite is superior to cubic zirconia in two ways: its hardness (8.5-9.25) and low SG (3.2). The former property results in facets that are as sometimes as crisp as a diamond's, while the latter property makes simulated moissanite somewhat harder to spot when unset (although still disparate enough to detect). However, unlike diamond and cubic zirconia, simulated moissanite is strongly [[birefringent]]. This manifests as the same "drunken vision" effect seen in synthetic rutile, although to a lesser degree. All simulated moissanite is cut with the table perpendicular to the optic axis in order to hide this property from above, but when viewed under magnification at only a slight tilt the doubling of facets (and any inclusions) is readily apparent.
The inclusions seen in simulated moissanite are also characteristic: most will have fine, white, subparallel growth tubes or needles oriented perpedicular to the stone's table. It is conceivable that these growth tubes could be mistaken for laser drill holes that are sometimes seen in diamond (see [[diamond enhancement]]), but the tubes will be noticeably doubled in simulated moissanite due to its birefringence. Like synthetic rutile, current simulated moissanite production is also plagued by an as of yet inescapable tint, which is usually a brownish green. A limited range of fancy colors have been produced as well, the two most common being blue and green. Jewel-quality simulated moissanite is produced by only one company, [[Charles & Colvard]]. Its limited availability makes simulated moissanite about 120 times more expensive than cubic zirconia.
== Natural simulants ==
Natural [[mineral]]s that (when cut) optically resemble white diamonds are rare, because the trace impurities usually present in natural minerals tend to impart color. The earliest simulants of diamond were colorless [[quartz]], [[topaz]], and [[beryl]] ([[goshenite]]); they are all common minerals with above-average hardness (7–8), but all have low RIs and correspondingly low dispersions. Well-formed quartz crystals are sometimes offered as "diamonds," a popular example being the so-called "[[Herkimer diamond]]s" mined in [[Herkimer County, New York]]. Topaz's SG (3.50–3.57) also falls within the range of diamond.
From a historical perspective, the most notable natural simulant of diamond is [[zircon]]. It is also fairly hard (7.5), but more importantly shows perceptible fire when cut, due to its high dispersion of 0.039. Colorless zircon has been mined in [[Sri Lanka]] for over 2,000 years; prior to the advent of modern [[mineralogy]], colorless zircon was thought to be an inferior form of diamond. It was called "Matara diamond" after its source location. It is still encountered as a diamond simulant, but differentiation is easy due to zircon's anisotropy and strong [[birefringence]] (0.059). It is also notoriously brittle and often shows wear on the girdle and facet edges.
Much less common than colorless zircon is colorless [[scheelite]]. Its dispersion (0.026) is also high enough to mimic diamond, but although it is highly lustrous its hardness is much too low (4.5–5.5) to maintain a good polish. It is also anisotropic and fairly dense (SG 5.9–6.1). Synthetic scheelite produced via the Czochralski process is available, but it has never been widely used as a diamond simulant. Due to the scarcity of natural gem-quality scheelite, synthetic scheelite is much more likely to simulate it than diamond. A similar case is the orthorhombic [[carbonate]] [[cerussite]], which is so fragile (very brittle with four directions of good cleavage) and soft (hardness 3.5) that it is never seen set in jewelry, and only occasionally seen in gem collections because it is so difficult to cut. Cerussite gems have an adamantine luster, high RI (1.804–2.078), and high dispersion (0.051), making them attractive and valued collector's pieces. Aside from softness, they are easily distinguished by cerussite's high density (SG 6.51) and anisotropy with extreme birefringence (0.271).
Due to their rarity fancy-colored diamonds are also imitated, and zircon can serve this purpose too. Applying heat treatment to brown zircon can create several bright colors: these are most commonly sky-blue, golden yellow, and red. Blue zircon is very popular, but it is not necessarily color stable; prolonged exposure to ultraviolet light (including the UV component in sunlight) tends to bleach the stone. Heat treatment also imparts greater brittleness to zircon and characteristic inclusions.
Another fragile candidate mineral is [[sphalerite]] (zinc blende). Gem-quality material is usually a strong yellow to honey brown, orange, red, or green; its very high RI (2.37) and dispersion (0.156) make for an extremely lustrous and fiery gem, and it is also isotropic. But here again, its low hardness (2.5–4) and perfect dodecahedral cleavage preclude sphalerite's wide use in jewelry. Two calcium-rich members of the [[garnet]] group fare much better: these are [[grossularite]] (usually brownish orange, rarely colorless, yellow, green, or pink) and [[andradite]]. The latter is the rarest and most costly of the garnets, with three of its varieties—[[topazolite]] (yellow), [[melanite]] (black), and [[demantoid]] (green)—sometimes seen in jewelry. Demantoid (literally "diamond-like") especially has been prized as a gemstone since its discovery in the [[Ural Mountains]] in 1868; it is a noted feature of antique [[Russia]]n and [[Art Nouveau]] jewelry. [[Titanite]] or sphene is also seen in antique jewelry; it is typically some shade of chartreuse and has a luster, RI (1.885–2.050), and dispersion (0.051) high enough to be mistaken for diamond, yet it is anisotropic (a high birefringence of 0.105–0.135) and soft (hardness 5.5).
Discovered the 1960s, the rich green [[tsavorite]] variety of grossular is also very popular. Both grossular and andradite are isotropic and have relatively high RIs (ca. 1.74 and 1.89, respectively) and high dispersions (0.027 and 0.057), with demantoid's exceeding diamond. However, both have a low hardness (6.5–7.5) and invariably possess inclusions atypical of diamond—the [[byssolite]] "horsetails" seen in demantoid are one striking example. Furthermore, most are very small, typically under 0.5 carats (100 mg) in weight. Their lusters range from vitreous to subadamantine, to almost metallic in the usually opaque melanite, which has been used to simulate black diamond. Some natural spinel is also a deep black and could serve this same purpose.
== Composites ==
Because strontium titanate and glass are too soft to survive use as a ring stone, they have been used in the construction of composite or ''doublet'' diamond simulants. The two materials are used for the bottom portion (pavilion) of the stone, and in the case of strontium titanate, a much harder material—usually colorless synthetic spinel or sapphire—is used for the top half (crown). In glass doublets, the top portion is made of [[almandine]] garnet; it is usually a very thin slice which does not modify the stone's overall body color. There have even been reports of diamond-on-diamond doublets, where a creative entrepreneur has used two small pieces of rough to create one larger stone.
In strontium titanate and diamond-based doublets, an [[epoxy]] is used to adhere the two halves together. The epoxy may fluoresce under UV light, and there may be residue on the stone's exterior. The garnet top of a glass doublet is physically fused to its base, but in it and the other doublet types there are usually flattened air bubbles seen at the junction of the two halves. A join line is also readily visible whose position is variable; it may be above or below the girdle, sometimes at an angle, but rarely along the girdle itself.
The most recent composite simulant involves combining a CZ core with an outer coating of laboratory created amorphous diamond. The concept effectively mimics the structure of a cultured pearl (which combines a core bead with an outer layer of pearl coating), only done for the diamond market. Brought to market under the 'Asha' brand name, the finished simulant provides a more lustrous and diamond-like look than plain CZ due to its usage of amorphous diamond.
== See also ==
*[[Diamond enhancement]]
*[[Diamond color]]
*[[Diamond cut]]
*[[Diamond clarity]]
*[[Material properties of diamond]]
*[[Synthetic diamond]]
== References ==
*Hall, Cally. (1994). ''Gemstones'', p. 63, 70, 121. Eyewitness Handbooks; Kyodo Printing Co., Singapore. ISBN 0-7737-2762-0
*Nassau, Kurt. (1980). ''Gems made by man'', pp. 203–241. [[Gemological Institute of America]]; Santa Monica, California. ISBN 0-87311-016-1
*O'Donoghue, Michael, and Joyner, Louise. (2003). ''Identification of gemstones'', pp. 12–19. Butterworth-Heinemann, Great Britain. ISBN 0-7506-5512-7
*Pagel-Theisen, Verena. (2001). ''Diamond grading ABC: The manual'' (9th ed.), pp. 298–313. Rubin & Son n.v.; Antwerp, Belgium. ISBN 3-9800434-6-0
*Schadt, H. (1996). ''Goldsmith's art: 5000 years of jewelry and hollowware'', p. 141. Arnoldsche Art Publisher; Stuttgard, New York. ISBN 3-925369-54-6
*Webster, Robert, and Read, Peter G. (Ed.) (2000). ''Gems: Their sources, descriptions and identification'' (5th ed.), pp. 65–71. Butterworth-Heinemann, Great Britain. ISBN 0-7506-1674-1
[[Category:Diamond]]
[[Category:Gemstones]]
[[Category:Glass art]]
[[nl:Imitatiediamant]]