'''Passivation''' is the process of making a material "passive" in relation to another material prior to using the materials together. For example, prior to storing [[hydrogen peroxide]] in an [[aluminium]] container, the container can be passivated by rinsing it with a dilute solution of [[nitric acid]] and peroxide alternating with [[deionized water]]. The nitric acid and peroxide [[oxidize]]s and dissolves any impurities on the inner surface of the container, and the deionized water rinses away the acid and oxidized impurities. Another typical passivation process of cleaning stainless steel tanks involves cleaning with NaOH and citric acid followed by nitric acid (up to 20% at 120F) and a complete water rinse. This process will restore the film, remove metal particles, dirt, and welding generated compounds (e.g. oxides).
In the context of [[corrosion]], '''passivation''' is the spontaneous formation of a hard non-reactive surface film that inhibits further corrosion. This layer is usually an oxide or nitride that is a few atoms thick.
==Mechanisms of passivation==
Under normal conditions of [[pH]] and [[oxygen]] [[concentration]], passivation is seen in such materials as [[aluminium]], [[iron]], [[zinc]], [[magnesium]], [[copper]], [[stainless steel]], [[titanium]], and [[silicon]]. Ordinary [[steel]] can form a passivating layer in [[alkali]] environments, as [[rebar]] does in [[concrete]]. The conditions necessary for passivation are recorded in [[Pourbaix diagram]]s.
Some [[corrosion inhibitor]]s help the formation of a passivation layer on the surface of the metals to which they are applied.
==Electrochemical passivation processes ==
Some compounds, dissolving in solutions ([[chromate]]s, [[molybdates]]) form non-reactive and low solubility films on metal surfaces.
== Passivation of specific materials ==
[[Aluminium]] may be protected from oxidation by [[anodizing]] and/or allodizing (sometimes called ''Alodining''), or any of an assortment of similar processes. (See terminology, below.) In addition, stacked passivation techniques are often used for protecting aluminium. For example, chromating is often used as a sealant to a previously-anodized surface, to increase resistance to salt-water exposure of aluminium parts by nearly a factor of 2 versus simply relying on anodizing.
[[Iron]] based (ferrous) materials, including [[steel]], may be somewhat protected by promoting oxidation ("rust") and then converting the oxidation to a metalophosphate by using [[phosphoric acid]] and further protected by surface coating. As the uncoated surface is water-soluble a preferred method is to form [[manganese]] or [[zinc]] compounds by a process commonly known as [[parkerize|Parkerizing]]. Older, less-effective but chemically-similar electrochemical conversion coatings included [[bluing (steel)|bluing]], also known as black oxide.
[[Nickel]] can be used for handling elemental [[fluorine]], thanks to a passivation layer of nickel fluoride.
== Terminology for assorted passivation processes ==
[[Bluing (steel)|Bluing]], also known as black oxide, and sometimes called ''browning'' when used in reference to historical processes dating from the 18th Century, is a passivation coating for the surfaces of iron and steel objects. It is one of the oldest passivation processes.
Newer, proprietary (and/or trademarked) processes for conversion coatings include ''[[Parkerize|Parkerized]]'' for passivating steel, dating to roughly 1912, and ''Alodine'' for passivating aluminium; both are trademarked processes and are now owned by Henkel Surface Technologies. [http://automotive.henkel.com/Products/Coatings/],[http://automotive.henkel.com/Brands/Alodine/]
''Chem film'' is any generic [[chromate conversion coating]] used to passivate aluminium. One such example is
{{US patent|5304257}}. In general, however, ''chromate'' can also mean any of several chromate conversion coatings that can be applied to a much wider range of metals and alloys than just to aluminium. In recent years, chromate coatings have become less popular due to concerns over environmental pollution from using such processes.
''Iridite'' is another trademarked name of a whole family of proprietary conversion coatings owned by MacDermid. A competing conversion coating used on aluminium, that somewhat ameliorates the environmental pollution concerns caused by chromate coatings, it often appears as a slightly yellowish coating, of roughly the same color as a yellow highlighting pen used to mark text on paper. [http://www.macdermid.com/industrial/aluminum.html]
== Rationale for passivating aluminium ==
Aluminium naturally forms an oxide almost immediately that protects it from further oxidation in many environments. This naturally-occurring oxide provides no protection during exposure to any saltwater spray environments, such as occurs in areas near bodies of saltwater. In such coastal environments, unprotected aluminium will turn white, corrode, and largely vanish over periods of exposure as short as a few years. The only way to prevent this from occurring is to use a more robust conversion coating on aluminium surfaces that will not be affected by the saltwater atmosphere. Alodine, Iridite, and chem film coatings can provide varying amounts of protection for aluminium surfaces.
== Further reading ==
[[ASTM]] A967 provides advice for the passivation of stainless steel parts.
[[Chromate Conversion Coat]] (Chemical Film) Per [[MIL-C-5541]] For Aluminum and Aluminum Alloy Parts
==References==
A standard overview on black oxide coatings is provided in MIL-HDBK-205, ''Phosphate & Black Oxide Coating of Ferrous Metals''. Many of the specifics of Black Oxide coatings may be found in MIL-DTL-13924 (formerly MIL-C-13924). This Mil-Spec document additionally identifies various classes of Black Oxide coatings, for use in a variety of purposes for protecting ferrous metals against rust.
*{{Harvard reference | Surname=Budinski | Given=Kenneth G. | Title=Surface Engineering for Wear Resistance | Publisher=Prentice Hall | Place=[[Englewood Cliffs, New Jersey]] | Year=1988 | p. 48}}
*{{Harvard reference | Surname=Brimi | Given=Marjorie A. | Title=Electrofinishing | Publisher=American Elsevier Publishing Company, Inc. | Place=[[New York, New York]] | Year=1965 | pp. 62-63 }}.
==External links==
*[http://automotive.henkel.com/Products/Coatings/ Henkel Surface Technologies] Current owner of Parco-Lubrite (a manganese phosphating process, ''Parkerizing'' process) and other conversion coatings/passivation processes. (Parco is a registered trademark of Henkel Surface Technologies.)
*[http://www.finishing.com/Chemicals/macdermid.shtml MacDermid Industrial Products, Inc.] Owner of numerous trademarked passivation processes.
*[http://www.novelindia.com Novel Surface Treatments] `Fumeless' Pickling and Passivation Gel Chemicals for Stainless Steel
[[Category:Metallurgy]]
[[Category:Corrosion prevention]]
[[bg:Пасивиране]]
[[cs:Pasivace]]
[[de:Passivierung]]
[[es:Pasivación]]
[[fr:Passivation]]
[[it:Passivazione]]
[[he:פסיבציה]]
[[ja:不動態]]
[[pl:Pasywacja]]
[[pt:Passivação]]
[[ru:Пассивация (электрохимия)]]
[[uk:Пасивація]]